EPOXY ZINC RICH PRIMER
|
PRODUCT NUMBER |
No.1006 (EP-03) |
|
TYPE |
A three-pack, zinc rich epoxy paint based on Epoxy Resin Polyamide hardener with high zinc content. |
|
USES |
Anti-corrosive paint for protection of ships, bridges, tanks, petrol-chemical factories, oil refineries, power plant, pulp factories and general steel constructions, etc. |
|
CHARACTERISTICS |
1. Very fast drying with excellent adhesion. 2. Very good resistance to mechanical damage. 3. Excellent resistance to seawater. 4. Slight scorch by gas cutting and welding. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller. |
|
COLOR |
Gray |
|
FINISH |
Flat |
|
SPECIFIC GRAVITY |
Above 2.5kg/L (Mixture) |
| VISCOSITY | 90
 120 KU (Mixture 25℃ ) |
| DRYING TIME | (25 ) Set-to-touch
1/4 hr. Dry hard 6 hrs. |
| OVERCOATING INTERVALS | Min. 8
hrs. (25℃ ) |
| FILM THICKNESS | Max. 6 months Wet 54~126 microns Dry 30~70 microns |
| SOLIDS (by Weight) | Above 80.00% (Mixture) |
| THEORETICAL COVERAGE | 7.9 m2 /L
3.1 m2 /KG 30  m2/GL
(WFT:126microns) |
| THINNER | SP-12 Epoxy Thinner |
| THINNING RATE | 5 ~ 20 (by wt.) |
|
SUBSEQUENT COATS |
Topcoats of Epoxy, Polyurethane, Vinyl or Chlorinated Rubber system. |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
MIXING RATIO |
Base: Hardener: Zinc Dust = 15: 9: 75 (by wt.) |
|
POT LIFE |
8
hrs. (Mixture) (25 |
|
NOTE |
1.Pour the hardener into the base with constant stirring. After all the hardener is added, add zinc dust gradually under constant agitation, and then pass through 80mesh filter. 2.The loose white materials such as zinc oxide, zinc hydroxide or zinc carbonate, etc. formed on weather-exposed film must be removed before subsequent coating. 3.Remove any soap, dust, rust, grease, old paint surface or any salt-containing chemicals before coating. 4.When used inside tanks, sufficient ventilation must be provided. 5.Keep stirring during application. |
) 
|
|
|
|
 |
|
|
|