HIGH SOLIDS EPOXY COATING
|
|
| PRODUCT NUMBER | 1061（EP-999） |
|
TYPE |
A two-pack,
high solids paint based on epoxy resin dual-use as a topcoat or primer. |
|
USES |
Used for ships, bridges, storage tanks and general steel structures to dual-use as topcoat or primer. |
|
CHARACTERISTICS |
1. Tough and hard film with excellent abrasion resistance. 2. Excellent water resistance. 3. With good penetration and inclusive on wet or rust surface of steel. 4. Excellent resistance to oils and chemicals 5. Can be coated in or can be coated with a variety of coatings, the best service and green paint. 6. Suitable used for the cereal tanks. |
|
FINISH |
Semi-flat |
|
COLOR |
White gray brown and Silver |
|
FLASH POINT |
Above 14℃（57℉） |
|
SPECIFIC GRAVITY |
1.30 (mixture) 1.10（silver） |
|
VISCOSITY |
100~120 KU (mixture, 25℃) |
| DRYING TIME | Set-to-touch 4
hrs. Dry hard 8 hrs. Fully dried 7 days |
| FILM THICKNESS | Wet 156~250 microns（6.2~10.0 mil） Dry 125~200 microns（5.0~8.0 mil） |
|
VOLUME SOLIDS |
80% （silver : 88%） |
|
THEORETICAL COVERAGE |
4.0~6.0 ㎡/L |
|
OVERCOATING INTERVALS |
Min. 12 hrs. |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~10% |
| PRECEDING COATS | No.1006 Epoxy Zinc rich Primer (EP-03) No.1011 Inorganic Zinc Rich Primer (IZ-01) No.700 One-pack Polyurethane Maintenance Primer No.1020 Epoxy Alloy Pimer No. 1075 Epoxy Aluminum Tripolyphosphate Primer |
| SUBSEQUENT COATS | Epoxy, Vinyl, PU or CR system |
|
MIXING RATIO |
Base: Hardener = 87: 13 (by wt.) |
|
POT LIFE |
2 hrs. (mixture, 25℃) |
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. |
| APPLICATION METHOD | Airless Spray, Brush, Roller |
| FOR AIRLESS SPRAY | Tip size 0.021” ~ 0.029” Air pressure 5 ~ 6 Kg/㎡ Pump ratio 33 : 1 or greater |
|
NOTE |
1. Mix base and
hardener according to the mixing ratio and stir thoroughly. 2. All equipment must be cleaned immediately after use. 3. When used inside tanks, and sufficient ventilation must be provided. |
|
|
|
|
 |
|
|
|