EPOXY-TAR, HB |
|
PRODUCT NUMBER |
1004 (EP-06) |
|
TYPE |
A two-pack, high build type anti-corrosive paint based on coal tar and epoxy resin with hardener. |
|
USES |
Used for coastal facilities, ballast tanks, bridges, chemical plants, water tunnel, underground water pipelines, power plant inlet and outlet cooling water steel pipes, sewage exhaust steel pipes etc. |
|
CHARACTERISTICS |
1. High build (250µ film can be obtained by one coat spray). 2. Tough and hard film, excellent abrasion resistance. 3. Excellent resistance to water, sea water, oils and chemicals. 4. Very good resistance to galvanic action. 5. Relatively low cost. |
|
FINISH |
Semi-gloss |
|
COLOR |
Black or brown |
|
MASS DENSITY |
Above 1.4 Kg/L (mixture) |
|
VISCOSITY |
95~115 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 5 hrs. Dry hard 24 hrs. Fully cured 7 days. (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 450 microns Dry 250 microns |
|
THEORETICAL COVERAGE |
8.4 ㎡/Gal 2.2 ㎡/L 1.5 ㎡/Kg |
|
OVERCOATING INTERVALS |
Min. 18 hrs. Max. 5 days (25℃) or 3 days (30℃) |
|
MIXING RATIO |
Base : hardener = 90.5 : 9.5 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 70% (mixture) |
|
POT LIFE |
5 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~10% (cleaning tools excluded) |
|
PRECEDING COATS |
Steel: No.908 Wash Primer (SP-01/02) No.1006 Epoxy Zinc Rich Primer (EP-03) No.1075 Epoxy Aluminum Tripolyphosphate Primer Concrete: No.1073 Epoxy Clear Cement Primer |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Spray, Brush |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. 7. Do not apply any colored paints on this product due to easy to seep coal tar. |
|
|
|
|
 |
|
|
|