EPOXY RED LEAD PRIMER

PRODUCT NUMBER

1007 (EP-01)

TYPE

A two-pack, high performance anti-corrosive primer based on epoxy resin and hardener with red lead pigment.

USES

Used for the steel structures, such as bridges, water canal, storage tanks, factory equipments etc.

CHARACTERISTICS

1. Tough and hard film with very good adhesion.

2. Excellent resistance to water and sea water.

3. Very good oils resistance.

4. Excellent rust preventive properties.

5. Excellent resistance to mechanical damage.

FINISH

Flat

COLOR

Orange

HIDING POWER

Above 10 ㎡/L (mixture)

MASS DENSITY

Above 1.5 Kg/L (mixture)

VISCOSITY

70~90 KU (mixture, 25℃)

DRYING TIME

Set-to-touch 1.5 hrs. Dry hard 6 hrs. Fully cured 7 days (25℃)

OPTIMUM FILM THICKNESS

Wet 100 microns Dry 50 microns

THEORETICAL COVERAGE

38.0 ㎡/Gal 10.0 ㎡/L 6.3 ㎡/Kg

OVERCOATING INTERVALS

Min. 8 hrs.

MIXING RATIO

Base : hardener = 93 : 7 (by wt.)

NON-VOLATILE CONTENT

Above 70.0% (mixture)

POT LIFE

8 hrs. (mixture, 25℃)

THINNER

No.1005 Epoxy Thinner (SP-12)

THINNING RATE

5~10 ％ (cleaning tools excluded)

SUBSEQUENT COATS

Epoxy, Vinyl, Chlorinated Rubber or PU system

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

APPLICATION METHOD

Airless Spray, Brush

NOTE

1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use.

2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly.

3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried.

4. All equipment must be cleaned immediately after use.

5. When used inside tanks, sufficient ventilation must be provided.