RED OXIDE SURFACER
|
||
|
PRODUCT NUMBER |
902 |
|
|
TYPE |
Red oxide rust prevention primer based on phenolic resin and dried oil with high quality anti-rust pigment. |
|
|
|
||
|
USES |
Used for vehicle and mechanical facilities. |
|
|
CHARACTERISTICS |
1. Fast drying. 2. Excellent resistance to water and rust. 3. Good adhesion and abrasion resistance. |
|
|
FINISH |
Flat |
|
|
COLOR |
Red |
|
|
HIDING POWER |
Above 20 m2/L |
|
|
MASS DENSITY |
Above 1.4 Kg/L |
|
|
VISCOSITY |
80~100 KU (25℃ |
|
|
DRYING TIME |
Set-to-touch 15 minutes Dry hard 2 hrs.
(25 |
|
| OPTIMUM FILM THICKNESS |
Wet 85 microns Dry 40 microns |
|
| THEORETICAL COVERAGE | 44.7  m2/Gal 11.8 m2/L 8.4 m2/Kg |
|
| OVERCOATING INTERVALS | Min. 3 hrs. (25℃ ) | |
| NON-VOLATILE CONTENT | Above 60% | |
| THINNER | No.805 Paint Thinner  OM-07 |
|
| THINNING RATE | 5~10%  cleaning for tools not included  |
|
| SUBSEQUENT COATS | No.903 Gray Surfacer, Ready-Mixed Paints, Synthetic Enamels, Hammer Tone Paints | |
| PRECEDING COATS | No.908 Wash Primer  SP-01/02  |
|
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. | |
| APPLICATION METHOD | Spray, Brush | |
| NOTE | 1. Before application, stir paint evenly, and when paint is too thick, thinner within specified quantity can be added. 2. Adhered moisture, grease, dirt, damaged or loose old paint and corrosive salts on substrate must be cleaned thoroughly. 3. Avoid applying the paint in
rainy, humid weather or substrate temperature excessively high to 40 |
|
) 
℃)
or low to 10
.
|
|
|
|
 |
|
|
|