EPOXY SPLASH ZONE CLADING |
|
|
PRODUCT NUMBER |
1085 |
|
TYPE |
A two-pack, high performance coating based on solvent-less putty-like epoxy resin and hardener with additives, it can self-curing in the water for protection against the corrosion. |
|
USES |
Used for the splash zone of coast and harbor facilities, or for the steel and concrete of the underwater area. |
|
CHARACTERISTICS |
1. Can easy to apply in water with good adhesion. 2. Minimal shrinkage after drying, no pinhole, and once is complete. 3. Excellent resistance to abrasion and impact. 4. Excellent resistance to sea water, alkalis and solvents. |
|
FINISH |
Flat |
|
COLOR |
Blue, black |
|
MASS DENSITY |
Above 1.5 Kg/L (mixture) |
|
VISCOSITY |
Paste (mixture) |
|
DRYING TIME |
Set-to-touch 1 hr. Dry hard 3 hrs. Fully cured 7days (25℃) |
|
OPTIMUM FILM THICKNESS |
Above 5 m/m |
| OVERCOATING INTERVALS | Min. 4 hrs. |
|
MIXING RATIO |
Base : hardener = 25 : 18 (by wt.) |
|
VOLUME SOLIDS |
100% |
| THEORETICAL COVERAGE | 8.0 Kg/㎡ @ 5 m/m |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) (Only for cleaning tools) |
|
THINNING RATE |
Not available |
|
POT LIFE |
30 minutes (mixture, 25℃) |
| SURFACE TREATMENT | Steel: Removed all loose rust, soil, grease and other dirt from substrate, using power tools to reach SIS St3 or by manual way to reach SIS St2, or by dry blasting to reach SIS Sa 2 1/2 for very serious environmental conditions, wet blasting can also. Concrete: Remove all grease, other dirt from surface, or to treat with sand blasting. |
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. |
| APPLICATION METHOD | Manual troweling, hand applying |
|
NOTE |
1. All equipment must be cleaned before use. 2. Mix base and hardener according to the mixing ratio and stir thoroughly. 3. Paint in the stirring can not be mixed with sea water or tap water. 4. Use wet hands to take a small amount of mixture to smear evenly on the substrate (wetting the manual method). 5. The surface of steel, aluminum, stainless steel or cement substrate must have apposite roughness. 6. All substrate must be cleaned thoroughly without any dirt to affect adhesion. 7. All equipment must be cleaned immediately after use. |
|
|
|
|
 |
|
|
|