EPOXY NON-SLIP DECK COATING |
|
| PRODUCT NUMBER | 1071 |
| TYPE | A two-pack, non-slip deck paint based on epoxy resin and hardener with quartz sand. |
|
USES |
Used for deck and cement floor to resist acids and alkalis. |
| CHARACTERISTICS | 1. Hard and tough film with anti-slip properties. 2. Excellent resistant to water and sea water. 3. Excellent resistance to abrasion and electronic insulation. 4. Excellent resistance to oils, solvents and chemicals |
|
FINISH |
Gloss and coarse |
|
COLOR |
Red Oxide, Gray, Black and Green |
|
MASS DENSITY |
Above 1.5 Kg/L (mixture) |
|
VISCOSITY |
Paste (mixture, 25℃) |
| DRYING TIME | Set-to-touch 2 hrs. Dry hard 12 hrs. Fully cured 7 days. (25℃) |
|
OPTIMUM FILM THICKNESS |
Approx. 1 m/m of rough surface |
|
THEORETICAL COVERAGE |
2.5 ㎡/Gal 0.66 ㎡/L 0.42 ㎡/Kg |
|
OVERCOATING INTERVALS |
Min. 8 hrs. Max. 2 days (25℃) |
|
MIXING RATIO |
Base : Hardener = 95 : 5 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 60% (mixture) |
|
POT LIFE |
5 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
0~5% (cleaning tools excluded) |
| PRECEDING COATS | No.1006 Epoxy Zinc Rich Primer (EP-03) No.1007 Epoxy Red Lead Primer (EP-01) No.1008 Epoxy Zinc Chromate Primer (EP-09) No.1009 Epoxy Red Oxide Primer (EP-02) No.1011 Inorganic Zinc Rich Primer (IZ-01) |
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. |
| APPLICATION METHOD | Brush, Roller, Funnel spray |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. |
|
|
|
|
 |
|
|
|