EPOXY M.I.O. PRIMER
|
|
|
PRODUCT NUMBER |
1050 (EP-20) |
|
TYPE |
A two pack, high performance anti-corrosive intermediate primer based on epoxy resin and special hardener with mica flakes iron oxide and aluminum pigments. |
|
USES |
Used for steel structures such as bridges, water canal, plant equipments, storage tanks etc. |
|
CHARACTERISTICS |
1. Tough and hard film with very good adhesion. 2. Excellent resistance to water and sea water. 3. Very good oils resistance. 4. Excellent rust preventive properties. 5. Excellent resistance to mechanical damage. 6. Very good resistance to ultraviolet ray penetration. |
|
FINISH |
Flat |
|
COLOR |
Silver red, grey |
|
HIDING POWER |
Above 10 ㎡/L (mixture) |
|
MASS DENSITY |
Above 1.4 Kg/L (mixture) |
|
VISCOSITY |
75~95 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 1.5 hrs. Dry hard 6 hrs. Fully Cured 7 days (25℃) |
| OPTIMUM FILM THICKNESS | Wet 200
microns Dry 100 microns |
| THEORETICAL COVERAGE | 18.9 ㎡/Gal 5.0 ㎡/L 3.57 ㎡/Kg |
| OVERCOATING INTERVALS | Min. 16 hrs. Max. 90 days (25℃) |
|
MIXING RATIO |
Base : hardener = 91 : 9 (by wt.) |
| NON-VOLATILE CONTENT | Above 65% |
|
POT LIFE |
8 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~10% (cleaning tools excluded) |
|
PRECEDING COATS |
Epoxy system or No.1011 Inorganic Zinc Rich Primer (IZ-01) |
|
SUBSEQUENT COATS |
Epoxy, Vinyl, CR or PU system |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Brush, Airless spray |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly. 2. Adhered moisture, grease, and dirt on substrate must be cleaned thoroughly. 3. Avoid applying the paint in rainy weather and particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. |
|
|
|
|
 |
|
|
|