WATER-BASED EPOXY ALUMINUM TRIPOLYPHOSPHATE PRIMER
|
PRODUCT NUMBER |
1035 |
|
TYPE |
A two pack, water-based anti-corrosive paint based on epoxy resin with aluminum tripolyphosphate non-pollution pigment and hardener. |
|
USES |
Used for exposed steel structure of bridge, storage tank, ship, cabin etc. |
|
CHARACTERISTICS |
1. Low stench, no fire danger because the thinner is the water. 2. Excellent coupling force and rust preventive properties and non-pollution. 3. Low shrinkage, high toughness and good adhesion. 4. Excellent resistance to water and chemicals. |
|
FINISH |
Flat |
|
COLOR |
White, brown, green |
|
MASS DENSITY |
Above 1.2 Kg/L (mixture) |
|
VISCOSITY |
80~100 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 2 hrs. Dry hard 4 hrs. Fully cured 7 days (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 110 microns Dry 50 microns |
|
THEORETICAL COVERAGE |
34.4 ㎡/Gal 9.1 ㎡/L |
|
OVERCOATING INTERVALS |
Min. 10 hrs. Max. 14 days |
|
MIXING RATIO |
Base : hardener = 92. : 8 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 50% (mixture) |
|
POT LIFE |
Above 4 hrs. (mixture, 25℃) |
|
THINNER |
Tap water |
|
THINNING RATE |
0~5% (cleaning tools excluded) |
|
APPLICATION METHOD |
Airless Spray, Spray, Brush |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. It also can be used inside the airtight space, but proper ventilation is good for dryingtime. All equipment must be cleaned immediately after use. 4. Since without the stable glue time, so please follow the pot life when applying. 5. Avoid applying the paint in rainy weather or relative humidity exceeded 85%. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. |
|
|
|
|
 |
|
|
|