EPOXY VARNISH |
|
|
PRODUCT NUMBER |
1010 |
|
TYPE |
A two-pack, waterproof and alkalis resistance clear paint based on epoxy resin and hardener. |
|
USES |
Used for cement wall, cement pipelines and cement products. |
|
CHARACTERISTICS |
1. Excellent resistance to water, sea water and sewage. 2. Excellent resistance to acids and alkalis. 3. Tough and hard film with very good adhesion. 4. Excellent resistance to mechanical damage. |
|
COLOR |
Transparent liquid |
|
MASS DENSITY |
Above 1.0 Kg/L (mixture) |
|
VISCOSITY |
60~80 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 2 hrs. Dry hard 10 hrs. Fully cured 7 days (25℃) |
| OPTIMUM FILM THICKNESS | Wet 45 microns Dry 25 microns |
| THEORETICAL COVERAGE | 84.0 ㎡/Gal 22.2 ㎡/L 22.2 ㎡/Kg |
| OVERCOATING INTERVALS | Min. 12 hrs. Max. 5 days (25℃) or 3 days(30℃) |
|
MIXING RATIO |
Base : hardener = 83.3 : 16.7 (by wt.) |
| NON-VOLATILE CONTENT | Above 55% (mixture) |
|
POT LIFE |
4 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
10~25% (depending on substrate) |
|
PRECEDING COATS |
No.1073 Epoxy Clear Cement Primer |
|
SUBSEQUENT COATS |
No.1001 Epoxy Topcoat (EP-04) |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. 7. The paint film exposed to the sun for a long-term does have yellowing and chalking phenomenon that is without affect the quality of paint film. |
|
|
|
|
 |
|
|
|