EPOXY RED OXIDE PRIMER |
|
PRODUCT NUMBER |
1009 (EP-02) |
|
TYPE |
A two-pack, anti-corrosive intermediate primer based on epoxy resin and hardener with red oxide pigment. |
|
USES |
Used for steel structures, such as bridges, steel frame, storage tanks, plant facilities etc. |
|
CHARACTERISTICS |
1. Excellent resistance to water and sea water. 2. Excellent resistance to mechanical damage. 3. Excellent resistance to oils, solvents and corrosion. 4. Tough and hard film with very good adhesion. 5. Relative low cost. |
|
FINISH |
Flat |
|
COLOR |
Reddish brown |
|
HIDING POWER |
Above 15 ㎡/L (mixture) |
|
MASS DENSITY |
Above 1.45 Kg/L (mixture) |
|
VISCOSITY |
75~85 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 1 hr. Dry hard 10 hrs. Fully cured 7 days (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 85 microns Dry 45 microns |
|
THEORETICAL COVERAGE |
44.5 ㎡/Gal 11.76 ㎡/L 8.1 ㎡/Kg |
|
OVERCOATING INTERVALS |
Min. 8 hrs. |
|
MIXING RATIO |
Base : hardener = 92 : 8 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 65% (mixture) |
|
POT LIFE |
5 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
0~5% (cleaning tools excluded) |
|
PRECEDING COATS |
No.1006 Epoxy Zinc Rich Primer (EP-03) No.1011 Inorganic Zinc Rich Primer (IZ-01) |
|
SUBSEQUENT COATS |
Epoxy, Vinyl, Chlorinated Rubber or PU system |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. |
|
|
|
|
 |
|
|
|