EPOXY COATING, SOLVENTLESS No.1015

EPOXY COATING, SOLVENTLESS

PRODUCT NUMBER

1015

TYPE

A two-pack finish coating based on special solvent-less epoxy resin and hardener with chemicals resistance pigments.

USES

Anti-corrosive paint for chemical plants, power plants, steel factories and lining of tanks.

CHARACTERISTICS

1. Tough and hard film with very good adhesion.

2. Brush one coat can obtain above 200 microns of no pinholes paint film.

3. Excellent water and oil resistance

4. Excellent chemical resistance and anticorrosion.

5. Excellent mechanical wear resistance and electric insulation.

GLOSS

Above 85%

COLOR

Limited, please refer to color card

HIDING POWER

Above 8 m2/L (mixture, depending on colors)

DENSITY

Above 1.35 Kg/L (mixture)

VISCOSITY

90 ~ 110 KU (25 ℃)

DRYING TIME

Set-to-touch 6 hrs. Dry hard 18 hrs. Full Dry 7 days (25 ℃).

OPTIMUM FILM THICKNESS

Wet 375 microns Dry 350 microns

THEORETICAL COVERAGE

10.2 ㎡/Gal 2.7 m2/L 2.3 m2/Kg

OVERCOATING INTERVALS

Min. 24 hrs. Max. 2 days (25 ℃)

MIXING RATIO

Base : Hardener = 80 : 20(by weight)

NON-VOLATILE CONTENT

Above 95% (mixture)

POT LIFE

30 minutes ( 25 ℃)

THINNER

No.1005 Epoxy Thinner(SP-12)(cleaning tools only)

PRECEDING COATS

No.1073 Epoxy Clear Cement Primer(or other suggested type)

STORAGE SHELF LIFE

Minimum 1 year under normal storage conditions.

APPLICATION METHOD

Trowel and brush.

NOTE

1. Mix base and hardener according to mixing ratio and stir thoroughly then use completely in five minutes.

2. Adhered moisture, grease, dirt, rusts and corrosive salts on substrate must be cleaned thoroughly.

3. Avoid applying the paint in rainy weather or humidity above 85% RH, particularly a wet surface must be thoroughly dried.

4. All equipments must be cleaned immediately after use.

5. When directly apply on the surface of cement products, the surface must be completely dried.

6. When overcoating interval is exceeded, the paint film must be roughened to insure adhesion.