GALVANIZING PAINT |
||
|
PRODUCT NUMBER |
1018 |
|
|
TYPE |
One-pack high performance corrosion preventive paint based on special resin and pure zinc powder. |
|
|
USES |
Used for the steel structures in long potent rust prevention, such as storage tank, |
|
|
bridge, steel frame, power tower etc. |
||
|
CHARACTERISTICS |
1. Fast drying with good adhesion. 2. One-pack, without pot life and easy to application. 3. Very good resistance to mechanical damage. 4. Rust-proof ability, through three years of seaside exposure without rusting. 5. Surface of paint film scratched still has performance of inhibited rusting. |
|
|
FINISH |
Flat |
|
|
COLOR |
Gray |
|
|
MASS DENSITY |
Above 1.8 Kg/L |
|
|
VISCOSITY |
65~90 KU (25 |
|
|
DRYING TIME |
Set-to-touch 0.5 hr. Dry hard 1 hr. (Air dry) Fully cured 14 days (25℃) |
|
|
OPTIMUM FILM THICKNESS |
Wet 110 microns Dry 30 microns |
|
|
THEORETICAL COVERAGE |
34.4 |
|
|
OVERCOATING INTERVALS |
Min. 4 hrs. Max. 1 month |
|
|
NON-VOLATILE CONTENT |
Above 65% |
|
|
THINNER |
No.1069 Galvanizing Paint Thinner |
|
|
THINNING RATE |
10~20% |
|
|
SUBSEQUENT COATS |
Solvent-based Acrylic Paint, PU Paint, PU High-Solids Paint or Epoxy Paint |
|
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
|
APPLICATION METHOD |
Brush, Airless Spray. |
|
|
NOTE |
1. Before application, stir paint evenly. When paint is too thick, thinner can be added within specified quantity. 2. Application in normal conditions, one-coat spraying is enough, but in serious conditions, it is better to do two-coat spraying. 3. If you use in chemical industry zone and in atmosphere contained acidic gases places, the surface of paint film must be applied one acid resistance coating. 4. Adhered moisture, grease, rust, sludge and corrosive salts on substrate must be removed. 5. Avoid
applying the paint in rainy, humid weather or substrate temperature excessively
high to 40 |
|
℃) 
㎡/Gal 9.1 ㎡
/L 5.1 ㎡/Kg 
cleaning tools excluded
℃ or low to 10℃
. 
|
|
|
|
 |
|
|
|