EPOXY ZINC PHOSPHATE PRIMER |
|
| PRODUCT NUMBER | 1076 (EP-66) |
|
TYPE |
A two-pack, anti-corrosive paint based on epoxy resin with zinc phosphate pigment. |
|
USES |
Used for the exposed steel structures of petrochemical factory, power plant, coastal facility, storage tank. |
| CHARACTERISTICS | 1. Excellent
resistance to sea water. 2. Excellent rust preventive properties. 3. Tough and hard film with very good adhesion. 4. Excellent resistance to mechanical damage. 5. Very good resistance to oils and chemicals |
|
FINISH |
Flat |
|
COLOR |
White Gray, Brown |
|
FLASH POINT |
20℃ (68℉ mixture) |
|
MASS DENSITY |
Above 1.3 Kg/L (mixture) |
|
VISCOSITY |
70~85 KU (mixture, 25℃) |
| DRYING TIME | Set-to-touch 1 hr.
Dry hard 4 hrs. Fully cured 7 days (25℃) |
OPTIMUM FILM THICKNESS |
Wet 100~220 microns Dry 45~100 microns |
|
THEORETICAL COVERAGE |
37.8 ㎡/Gal 10.0 ㎡/L 7.4 ㎡/Kg (DFT: 45 microns) |
|
OVERCOATING INTERVALS |
Min. 8 hrs. (25℃) |
|
MIXING RATIO |
Base : Hardener = 92 : 8 (by wt.) |
|
NON-VOLATILE CONTENT |
Above 60% (mixture) |
|
POT LIFE |
8 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~15% (by wt.) |
| PRECEDING COATS | No.908 Wash Primer (SP-01/02) No.1006 Epoxy Zinc Rich Primer (EP-03) No.1011 Inorganic Rich Primer (IZ-01) No.1021 Cathozinc Shop Primer, Type-2 (SP-09) SP-08 Epoxy Non-Zinc Shop Primer |
| SUBSEQUENT COATS | Epoxy, Vinyl, Chlorinated Rubber or PU system. |
| FOR AIRLESS SPRAY | Tip Size 0.019"~0.021" Air Pressure 5~ 6 Kg/cm2 Pump Ratio 28 : 1 or greater |
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller. |
|
NOTE |
1. Mix base and
hardener according to the mixing ratio and stir thoroughly. 2. Avoid applying paint in rainy or humid weather and particularly a wet surface must be thoroughly dried. 3. All equipment must be cleaned immediately after use. 4. When used inside tanks, sufficient ventilation must be provided. |
|
|
|
|
 |
|
|
|