EPOXY MIDDLE COATING |
|
|
PRODUCT NUMBER |
1060 |
|
TYPE |
A two-pack, middle paint based on epoxy resin and special hardener with special pigment. |
|
USES |
Used for steel structures that have been coated with inorganic zinc rich primer, such as steel pipes, steel frame, bridges, plant facilities etc to prevent the blistering, also used for cement wall and cement products. |
|
CHARACTERISTICS |
1. Tough and hard film, rich flexible and adhesion. 2. Excellent adhesion with inorganic zinc rich primer, it can fill holes on surface of zinc rich paint to prevent topcoat to blistering. 3. Excellent abrasion resistance and electrical insulation. 4. Excellent resistance to oils, solvents and chemicals. |
|
FINISH |
Flat |
|
COLOR |
White, grey, reddish brown |
|
HIDING POWER |
Above 8 ㎡/L (mixture) |
|
MASS DENSITY |
Above 1.45 Kg/L |
|
VISCOSITY |
70~90 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 1.5 hrs. Dry hard 6 hrs. Fully cured 7 days (25℃) |
| OPTIMUM FILM THICKNESS | Wet 80 microns Dry 40 microns |
| THEORETICAL COVERAGE | 47.3 ㎡/Gal 12.5 ㎡/L 8.3 ㎡/Kg |
| OVERCOATING INTERVALS | Min. 8 hrs. |
|
MIXING RATIO |
Base : hardener = 92.1 : 7.9 (by wt.) |
| NON-VOLATILE CONTENT | Above 70% (mixture, 25℃) |
|
POT LIFE |
8 hrs. (mixture, 25℃) |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~15% (cleaning tools excluded) |
|
PRECEDING COATS |
Steel: No.1006 Epoxy Zinc Rich Primer (EP-03) No.1011 Inorganic Zinc Rich Primer (IZ-01) Concrete: No.1073 Epoxy Clear Cement Primer No.1073PC Epoxy Cement Primer No.1002 Epoxy Primer, white |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. |
|
|
|
|
 |
|
|
|