EPOXY TOPCOAT |
|
|
|
|
PRODUCT NUMBER |
1001(EP-04) / 1055 / 1056 |
|
TYPE |
A two-pack, heavy duty corrosion resistance paint based on epoxy resin and special hardener with weather and chemicals resistant pigment. |
|
USES |
Used for cement products and steel structures such as steel pipes, steel frame, bridges, plant facilities etc. |
|
CHARACTERISTICS |
1. Tough and hard film, rich flexible and adhesion. 2. Excellent resistance to water and sea water. 3. Excellent resistance to abrasion and mechanical damage. 4. Excellent resistance to oils, solvents and chemicals. |
|
FINISH |
Gloss |
|
COLOR |
Desired colors |
|
HIDING POWER |
Above 8.0 ㎡/L (mixture, depending on colors) |
|
MASS DENSITY |
Above 1.1 Kg/L (mixture, depending on colors) |
|
VISCOSITY |
70~95 KU (mixture, 25℃) |
|
DRYING TIME |
Set-to-touch 2hrs. Dry hard 10 hrs. Fully cured 7 days (25℃) |
|
OPTIMUM FILM THICKNESS |
Wet 100 microns Dry 40 microns |
|
THEORETICAL COVERAGE |
38.0 ㎡/GL 10.0 ㎡/L 9.0 ㎡/Kg |
|
OVERCOATING INTERVALS |
Min. 8 hrs. Max. 6 months |
|
MIXING RATIO |
Base : hardener = 92 : 8 (by wt, depending on colors.) |
|
NON-VOLATILE CONTENTS |
Above 60% (mixture) |
|
POT LIFE |
8 hrs. (mixture, 25℃) |
|
HEAT RESISTANCE |
Continuous 93℃ Intermittent 121℃ |
|
THINNER |
No.1005 Epoxy Thinner (SP-12) |
|
THINNING RATE |
5~10% (cleaning tools excluded) |
|
PRECEDING COATS |
Steel : No.1006(EP-03), No.1007(EP-01), No.1011(IZ-01), No.1050(EP-20), No.1075 No.1076(EP-66) |
|
|
Concrete: No.1073, No.1002, No.1060 |
|
STORAGE SHELF LIFE |
Minimum 1 year under normal storage conditions. |
|
APPLICATION METHOD |
Airless Spray, Brush, Roller. |
|
NOTE |
1. Mix base and hardener according to the mixing ratio and stir thoroughly then keep static about 10~20 minutes before use. 2. Adhered moisture, grease, dirt, dust, rust and corrosion salts on substrate must be removed thoroughly. 3. Avoid applying the paint in rainy weather or relative humidity exceeded 85%, particularly a wet surface must be thoroughly dried. 4. All equipment must be cleaned immediately after use. 5. When used inside tanks, sufficient ventilation must be provided. 6. When overcoating interval is exceeded, paint surface must be roughened to ensure adhesion. 7. The paint film exposed to the sun for a long-term does have chalking phenomenon that is without affect the quality of paint film. |
|
|
|
|
 |
|
|
|