M.I.O. PRIMER
|
|
|
PRODUCT NUMBER |
950 |
|
TYPE |
Rust prevention middle primer based on alkyd resin and special resin with mica flake iron oxide, aluminum powder pigments. |
|
USES |
Used for steel structures, bridges and storage tanks. |
|
CHARACTERISTICS |
1. Very fast drying with good adhesion. 2. Excellent resistance to water and oils. 3. Excellent rust resistance, dipping in 3% salt water for 120 hours, result had no abnormal. 4. Excellent ultraviolet resistance and permeability. |
|
FINISH |
Flat |
|
COLOR |
Silver Red |
|
HIDING POWER |
Above 20.0 m2/L |
|
MASS DENSITY |
Above 1.4 Kg/L |
|
VISCOSITY |
80~100 KU (25℃ |
|
DRYING TIME |
Set-to-touch 1 hr. Dry hard 3 hrs.
(25℃ |
| OPTIMUM FILM THICKNESS | Wet 125 microns Dry 50 microns |
| THEORETICAL COVERAGE | 30.3  m2/Gal
8.0  m2/L
5.3 m2/Kg |
| OVERCOATING INTERVALS | Min. 4 hrs. |
| NON-VOLATILE CONTENT | Above 60% |
| THINNER | No.805 Paint Thinner OM-07 |
| THINNING RATE | 5~10%  cleaning for tools not
included |
| PRECEDING COATS | No.904 Red Oxide Primer OP-95 No.905 High Red Lead Primer OP-91 No.906 Red Lead Primer OP-92 No.907 Zinc Chromate Primer OP-93 No.911 Red Lead Primer, General Purpose SP-70 No.920 LZI Primer OP-94 No.992 Aluminum Tripolyphosphate Primer |
| SUBSEQUENT COATS | Ready-Mixed Paints, Synthetic Enamels |
| STORAGE SHELF LIFE | Minimum 1 year under normal storage conditions. |
APPLICATION METHOD |
Spray, Brush, Roller |
| NOTE | 1. Before application, stir paint evenly, and when paint is too thick, thinner within specified quantity can be added. 2. Adhered moisture, grease, dirt, damaged or loose old paint and corrosive salts on substrate must be cleaned thoroughly. 3. Avoid applying the paint in
rainy, humid weather or substrate temperature excessively high to 40 4. Avoid applying to insufficient drying of previous paint coat. |
) 
) 
℃ or low to 10
℃.
|
|
|
|
 |
|
|
|