Supra SMP

Supra SMP

  • Globally Available

  • Complete U.S.WARRANTY SUPPORT Program

  • Tough and Abrasion Resistant Coating formulation

  • Superior Corrosion and Wet-stack protection

  • Specialty, Multi-coat, and High Build Systems Available

  • Long Term International Commercial and Industrial experience

System Overview

Supra SMP coil coating system manufactured and distributed globally by Continental Coatings Inc. and Yung Chi Paint and Varnish Manufacturing Company Ltd., is a Silicone Modified Polyester (SMP) coil coating system engineered for high end metal building product applications and challenging exterior environments that require long life and extended warranty coverage. Supra SMP system is formulated with a proprietary state of the art polyester resin and silicone polymer system, which is significantly more resistant to

U.V. radiation and natural weathering than traditional SMP paints. Supra SMP uses high quality long lasting organic, ceramic and metallic pigmentation to insure excellent exterior color fastness and coating service life. This system is also available in multiple coats and various specialty high build systems for custom projects and perforated applications. Supra SMP may be applied over the Universal PU-11 High Molecular Weight Urethane Primer or PU-30 High-build Urethane primer systems for extreme environment warranted building product applications.

Application Parameters

Supra SMP system is designed for trouble free high line speed coil coating line application and has been run worldwide under a very wide range of application parameters and substrate conditions. Standard topcoat DFT is .70-.80 mils, which allows for optimal application consistency, color stability and exterior performance. Supra SMP was formulated to provide improved stain resistance and cleanability as well as scratch resistance and surface toughness while maintaining the good system flexibility required for long term bend line corrosion performance. Supra SMP paint film is extra tough and can handle difficult roll forming and panel stacking and transport conditions. Superior primer corrosion resistance and substrate adhesion provide significantly enhanced protection against wet stack storage problems and cut edge and scratch corrosion.

Commercial Uses

Supra SMP system can be formulated in standard, medium, textured, and lowgloss/ low sheen finishes and supplied in wide range but limited color pallet. This premium coating supports an extended warranty and can be applied to a variety of adequately cleaned and treated metal substrates including: Hot Dipped Galvanized, ZnAl, Galfan®, ZAM®, and Aluminum. Supra SMP can be formulated with COOL ROOF ceramic pigment technology and can be formulatedtoexceedU.S.EnergyStar® requirements. It is most ideal for metal wall panels, Industrial and agricultural metal building components, commercial and residential Metal Roofing, and pre-engineered metal building system applications.

Supra SMP Premium SMP Coil Coating System Silicone Modified Polyester





Application Method

Reverse Roll Coat


PU11 HMW PU, PU30 High Build PU


Aluminum, HDG, Galvalume®, ZAM®


Standard clean and treat

Chrome, Zinc Phosphate, or approved non-chrome

ASTM D 4138

Dry Film Thickness

Top coat: 0.7 to 0.8 mils

Primer: 0.15 to 0.3 mils

Total system: 0.85 to 1.10 mils

ASTM D 4212

Viscosity (No. 4 Zahn cup)

25 to 35 seconds

ASTM D 1475

Weight Per Gallon

9.0 to 12.0 Pounds Per Gallon

ASTM D 2697

Solids Per Volume

50 to 55%

ASTM D 2369

Solids Per Weight

60 to 75%

Reducing Thinner

Reducing Solvent


ASTM D 3960

VOC (Theoretical)

3.0 to 4.0 Pounds Per Gallon

Clean-up Solvent


Coating Mileage

1069 to 1176 Sq. Ft. / Gallon

Peak Metal Temperature

435 F to 450 F





ASTM D 523

Specular Gloss at 60

6 to 85

ASTM D 3363

Pencil Hardness


ASTM D 4145


1T to 4T with no loss of adhesion

ASTM D 5402

Solvent Resistance (MEK Rubs)

100 +

ASTM D 3359

Cross Hatch Adhesion

No loss of adhesion

ASTM D 2794

Reverse Impact

Galvalume or HDG: 3x metal thickness inch-pounds, no loss of adhesion

Aluminum: 1.5x metal thickness inch-pounds, no loss of adhesion

ASTM B 117

Salt Spray Resistance 1,000 hrs. Salt Spray Resistance 2,000 hrs.

Galvalume or HDG: Creep from scribe < 1/8 inch (3mm), none or few #8 blisters

Aluminum: Creep from scribe < Creep from scribe

<1/8 inch (3mm), few #8 blisters

ASTM D 2244

ASTM D 4214

South Florida Exposure

Color: No more than 5 (E) Hunterunits at 90 vertical angle and 7 (E) unitsnon vertical

Chalk: Rating no less than 8 at 90 angle and 6 at non vertical angle

Film Integrity: 25 years, no blisters, peeling or cracking

ASTM D 870

Water Immersion 100 F 168 hrs.

No field blisters with minimal color change

ASTM D 1308

Chemical Resistance (15 mins.)

No significant color change (color dependent)


Flame Spread Classification

Class I or A

ASTM D 968

Abrasion Resistance

Total Sand = 35 +/- 5 liters (Dft dependent)